【Metal-Ceramic Composite Filter】
Metal Substrate |
O.D. |
Wall Thickness for Substrate |
Length |
Suggested Thread |
Filtration accuracy |
Titanium |
30mm 50mm 50mm |
2.5mm 2.5mm 2.5mm |
30cm 50cm 100cm |
M16 M24 M24 |
50nm @ 95% Retention Rate 0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate |
X/Hastelloy X |
30mm 50mm 50mm |
2.3mm 2.3mm 2.3mm |
30cm 60cm 100cm |
M16 M24 M24 |
0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate (50nm Product In Development) |
C-22/Hastelloy C-22 |
30mm 50mm 50mm |
2.5mm 2.5mm 2.5mm |
30cm 50cm 100cm |
M16 M24 M24 |
0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate (50nm Product In Development) |
Inconel 625 |
30mm 50mm 50mm |
2.3mm 2.3mm 2.3mm |
30cm 60cm 100cm |
M16 M24 M24 |
0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate (50nm Product In Development) |
Inconel 600 |
30mm 50mm 50mm |
2.5mm 2.5mm 2.5mm |
30cm 50cm 100cm |
M16 M24 M24 |
0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate (50nm Product In Development) |
Monel 400 |
30mm 50mm 50mm |
2.5mm 2.5mm 2.5mm |
30cm 50cm 100cm |
M16 M24 M24 |
0.2µm @ 99% Retention Rate 0.45µm @ 99% Retention Rate 1µm @ 99% Retention Rate (50nm Product In Development) |
【Suitable application environment】
Hydrochloric Acid (1.5M) |
Nitric Acid (1.5M) |
Sulfuric Acid (1.5M) |
Sodium Hydroxide (22%) |
Ethanol (99.5%) |
Isopropanol (99%) |
Acetone |
|
Titanium |
R |
N |
N |
R |
R |
R |
R |
Monel 400 |
R |
N |
R |
R |
R |
R |
R |
Inconel 625 |
R |
R |
R |
R |
R |
R |
R |
Hastelloy X |
R |
R |
R |
R |
R |
R |
R |
*The results were tested under static conditions for 48 hours at room temperature.
*R: Resistant
*N: Not Resistant.
*R: Resistant
*N: Not Resistant.